This study investigated the influence of dope extrusion rate (DER) and post-treatment effect on the morphology, permeation, and metal ion rejection by polyethersulfone/lithium bromide (PES/LiBr)-based hollow fiber (HF) membranes. HF fibers were spun with 2.25, 2.5, and 3.1 ratios of DER to bore fluid rate (BFR), wherein DER varied from 11.35, 12.5, to 15.6 mL/min with a fixed BFR (5 mL/min). Molecular weight cutoff (MWCO), pore size, water flux, and flux recovery ratio were determined, whereas lake water was used to observe the rejection rate of dissolved metallic ions. Results showed that with the increase of the DER wall thickness (WT), HFs increased from 401.5 to 419.5 um, and furthermore by the post-treatments up to 548.2 um, as confirmed by field emission scanning electron microscope (FESEM) analysis. Moreover, MWCO, pore size, and the pure water permeation (PWP) of the HF membranes decreased, while the separation performance for polyethylene glycol (PEG) solute increased with increasing DER. Post-treated HFs from 11.35 mL/min of DER showed 93.8% of MWCO value with up to 90% and 70% rejection of the arsenic and chromium metallic ions, respectively, in comparison with all other formulated HFs.
Keywords: PES; dope extrusion; hollow fiber; lake water; salt.