Tailoring Fe2O3-Al2O3 catalyst structure and activity via hydrothermal synthesis for carbon nanotubes and hydrogen production from polyolefin plastics

Andrei Veksha; Muhammad Zahin Bin Mohamed Amrad; Wen Qian Chen; Dara Khairunnisa Binte Mohamed; Satya Brat Tiwari; Teik-Thye Lim; Grzegorz Lisak

doi:10.1016/j.chemosphere.2022.134148

Tailoring Fe₂O₃-Al₂O₃ catalyst structure and activity via hydrothermal synthesis for carbon nanotubes and hydrogen production from polyolefin plastics

Chemosphere. 2022 Jun:297:134148. doi: 10.1016/j.chemosphere.2022.134148. Epub 2022 Feb 28.

Authors

Andrei Veksha¹, Muhammad Zahin Bin Mohamed Amrad², Wen Qian Chen², Dara Khairunnisa Binte Mohamed², Satya Brat Tiwari², Teik-Thye Lim², Grzegorz Lisak³

Affiliations

¹ Residues and Resource Reclamation Centre (R3C), Nanyang Environment and Water Research Institute, Nanyang Technological University, 1 Cleantech Loop, CleanTech One, 637141, Singapore. Electronic address: aveksha@ntu.edu.sg.
² Residues and Resource Reclamation Centre (R3C), Nanyang Environment and Water Research Institute, Nanyang Technological University, 1 Cleantech Loop, CleanTech One, 637141, Singapore; School of Civil and Environmental Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798, Singapore.
³ Residues and Resource Reclamation Centre (R3C), Nanyang Environment and Water Research Institute, Nanyang Technological University, 1 Cleantech Loop, CleanTech One, 637141, Singapore; School of Civil and Environmental Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798, Singapore. Electronic address: g.lisak@ntu.edu.sg.

PMID: 35240158
DOI: 10.1016/j.chemosphere.2022.134148

Abstract

Fe₂O₃-Al₂O₃ catalysts applied for conversion of polyolefin plastic waste into multi-walled carbon nanotubes (MWCNTs) and H₂ are typically produced by impregnation, co-precipitation or sol-gel synthesis at atmospheric pressure and temperatures below 100 °C. This study utilized hydrothermal conditions and established the role of precipitating agents (urea, N-methylurea and N,N'-dimethylurea) on properties and catalytic activity of Fe₂O₃-Al₂O₃ catalysts (Fe-u, Fe-mu and Fe-dmu, respectively). The precipitating agent played a key role in tailoring the properties, such as crystallization degree, surface area and reducibility. The precipitating agents influenced the yield and outer diameters of MWCNTs but did not affect graphitization degree. Among the synthesized catalysts, Fe-u had the largest surface area and preferential formation of the highly reducible α-Fe₂O₃ crystalline phase. As a result, Fe-u had the highest activity during conversion of pyrolysis gas from low-density polyethylene (LDPE) into MWCNTs, yielding 0.91 g·g^-1-catalyst MWCNTs at 800 °C as compared to 0.42 and 0.14 g·g^-1-catalyst using Fe-dmu and Fe-mu, respectively. Fe-dmu favored the growth of MWCNTs with smaller outer diameters. Fe-u demonstrated high efficiency during operation using a continuous flow of pyrolysis gas from a mixture of polyolefins (70 wt% polypropylene, 6 wt% LDPE and 24 wt% high density polyethylene) producing 4.28 g·g^-1-catalyst MWCNTs at 3.2% plastic conversion efficiency and a stable H₂ flow for 155 min (25-32 vol%). The obtained data demonstrate that the selection of an appropriate precipitating agent for hydrothermal synthesis allows for the production of highly active Fe₂O₃-Al₂O₃ catalysts for the upcycling of polyolefin plastic waste into MWCNTs and H₂.

Keywords: Hydrogen; Hydrothermal synthesis; Multi-walled carbon nanotubes; Plastic waste; catalyst.