The soft hybrid organic-inorganic structure of two-dimensional layered perovskites (2DLPs) enables broadband emission at room temperature from a single material, which makes 2DLPs promising sources for solid-state white lighting, yet with low efficiency. The underlying photophysics involves self-trapping of excitons favored by distortions of the inorganic lattice and coupling to phonons, where the mechanism is still under debate. 2DLPs with different organic moieties and emission ranging from self-trapped exciton (STE)-dominated white light to blue band-edge photoluminescence are investigated. Detailed insights into the directional symmetries of phonon modes are gained using angle-resolved polarized Raman spectroscopy and are correlated to the temperature-dependence of the STE emission. It is demonstrated that weak STE bands at low-temperature are linked to in-plane phonons, and efficient room-temperature STE emission to more complex coupling to several phonon modes with out-of-plane components. Thereby, a unique view is provided into the lattice deformations and recombination dynamics that are key to designing more efficient materials.
Keywords: 2D layered perovskites; Raman spectroscopy; organic cations; phonons; photoluminescence; self-trapped excitons; white light emission.
© 2022 The Authors. Small published by Wiley-VCH GmbH.