BFS-MK-based alkali-activated materials are well established as an alternative for sustainable and green construction. This work aims to collaborate and encourage the use of biomass ashes, such as sugarcane bagasse ash (SCBA), as a precursor in alkali-activated materials (AAM). This ash is a rich source of aluminosilicate, which is a primary requirement for this application. In addition, this waste is still an environmental liability, especially in developing countries, and with a large volume of annual production. Thus, in this research, alkali-activated pastes (AA) were produced using sugarcane bagasse ash (SCBA), granulated blast furnace slag (BFS) and metakaolin (MK) as precursors. In addition, environmental gains were encouraged with energy savings, with no extra reburn or calcination steps in the SCBA. Thus, the precursors were characterized by laser granulometry, X-ray fluorescence spectrometry (XRF), X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR). The pastes were produced by mixing the precursors with the activator, composed of a mixture of sodium hydroxide 8 mol/L and sodium silicate. Aiming to study the incorporation of SCBA, all samples have a precursor/activator ratio and a BFS/(BFS + MK) ratio constant of 0.6. The compressive strength analysis, FTIR, XRD, TGA, SEM and isothermal calorimetry analyses pointed out the occurrence of alkaline activation in all proposed samples for curing times of 7, 28 and 91 days. The sample GM0.6-BA0 (15% SCBA) achieved the highest compressive strength among the samples proposed (117.7 MPa, at 91 days), along with a good development of strength throughout the curing days. Thus, this work presents the properties of alkaline-activated pastes using SCBA as a sustainable and alternative precursor, seeking to encourage the use of raw materials and alternative waste in civil construction.
Keywords: alkali-activated paste; alternative precursor; ambient temperature curing; sugarcane bagasse ash.