The fire resistance of fiber-reinforced polymer reinforced concrete (FRP-RC) elements depends on the temperature performance of the original concrete member, the fire scenario, and FRP reinforcement behavior. In this study, fire resistance tests are described, along with the characteristics obtained during and after applying elevated temperatures, simulating the effects of fire. The tested beams were reinforced with basalt (BFRP) bars and with a hybrid composite of carbon fibers and basalt fibers (HFRP) bars. Fire tests were performed on full-scale beams, in which the midsections of the beams were heated from below (tension zone) and from the sides for two hours, after which the beams were cooled and subjected to flexural testing. BFRP-RC beams failed before the heating time was completed; the best failure was associated with a BFRP reinforced beam that failed approximately 108 min after heating. Contrary to the BFRP-RC samples, HFRP-RC beams were capable of resisting exposure to elevated temperatures for two hours, but showed a 70% reduction in strength capacity when compared to non-heated reference beams. According to the author, the higher resistance of HFRP-RC beams was the result of the thermal expansion coefficient of carbon fibers employed in HFRP, which "prestresses" the beams and enables smaller deflections. The preliminary findings of this study can increase the feasibility of using FRP materials for engineering purposes.
Keywords: FRP bars; FRP reinforced concrete members; basalt FRP; fiber reinforced polymers FRP; fire resistance of FRP-RC beams; hybrid FRP.