Improvements in tensile strength and impact resistance of concrete are among the most researched issues in the construction industry. The present study aims to improve the properties of concrete against impact loadings. For this purpose, energy-absorbing materials are used along with fibers that help in controlling the crack opening. A polymer-based energy-absorbing admixture, SBR latex, along with polypropylene fibers are used in this study to improve the impact resistance. Along with fibers and polymers, the effect of the size of aggregates was also investigated. In total, 12 mixes were prepared and tested against the drop weight test and the Charpy impact test. Other than this, mechanical characterization was also carried out for all the 12 concrete mixes. Three dosages of SBR latex, i.e., 0%, 4%, and 8% by weight of cement, were used along with three aggregates sizes, 19 mm down, 10 mm down, and 4.75 mm down. The quantity of polypropylene fibers was kept equal to 0.5% in all mixes. In addition to these, three control samples were also prepared for comparison. The mix design was performed to achieve a normal-strength concrete. For this purpose, a concrete mix of 1:1.5:3 was used with a water to a cement ratio of 0.4 to achieve a normal-strength concrete. The experimental study concluded that the addition of SBR latex improves the impact resistance of concrete. Furthermore, an increase in impact resistance was also observed for a larger aggregate size. The use of fibers and SBR latex is encouraged due to their positive results and the fact that they provide an economical solution for catering to impact strains. The study concludes that 4% SBR latex and 0.5% fibers with a larger aggregate size improve the resistance against impact loads.
Keywords: SBR latex; aggregate size effect; drop weight; impact resistance; polypropylene fibers.