A unique approach was utilized to develop multi-walled carbon nanotube (MWCNT) silver (Ag) membranes. MWCNTs were impregnated with 1 wt% Ag loading, which resulted in a homogeneous dispersion of Ag in MWCNTs. MWCNTs impregnated with Ag were then uniaxially compacted at two different pressures of 80 MPa and 120 MPa to form a compact membrane. Compacted membranes were then sintered at two different temperatures of 800 °C and 900 °C to bind Ag particles with MWCNTs as Ag particles also act as a welding agent for CNTs. The powder mixture was characterized by FESEM, thermogravimetric analysis, and XRD, while the developed samples were characterized by calculating the porosity of membrane samples, contact angle, water flux and a diametral compression test. The developed membranes showed overall large water flux, while maximum porosity was found to decrease as the compaction load and sintering temperature increased. The mechanical strength of the membranes was found to increase as the compaction load increased. The hydrophilicity of the membranes remained unchanged after the addition of Ag particles. The developed membranes would be useful for removing a variety of contaminants from water.
Keywords: impregnated MWCNTs; membranes; multi-walled carbon nanotubes; silver particles; water purification.