Ferroelectric bismuth-titanate nanoplatelets and nanowires with a new crystal structure

Nanoscale. 2022 Mar 7;14(9):3537-3544. doi: 10.1039/d2nr00307d.

Authors

Darko Makovec^{1

2}, Nina Križaj^{1

2}, Anton Meden³, Goran Dražić⁴, Hana Uršič⁵, Rok Kostanjšek⁶, Martin Šala⁴, Sašo Gyergyek¹

Affiliations

¹ Department for Materials Synthesis, Jožef Stefan Institute, Jamova 39, SI-1000 Ljubljana, Slovenia. darko.makovec@ijs.si.
² Jožef Stefan International Postgraduate School, Jamova 39, SI-1000 Ljubljana, Slovenia.
³ Faculty of Chemistry and Chemical Technology, University of Ljubljana, Večna pot 113, SI-1000 Ljubljana, Slovenia.
⁴ National Institute of Chemistry, Hajdrihova 19, SI-1000 Ljubljana, Slovenia.
⁵ Department for Electronic Ceramics, Jožef Stefan Institute, Jamova 39, 1000 Ljubljana, Slovenia.
⁶ Department of Biology, Biotechnical Faculty, University of Ljubljana, Jamnikarjeva 101, SI-1000 Ljubljana, Slovenia.

PMID: 35174842
DOI: 10.1039/d2nr00307d

Abstract

Two different morphologies of ferroelectric bismuth titanate (Bi₄Ti₃O₁₂) nanoparticles, i.e., nanoplatelets and nanowires, were synthesized by changing the concentration of NaOH during a hydrothermal treatment of precipitated Ti⁴⁺ and Bi³⁺ ions. The nanoparticles' crystal structures were characterized using atomic-resolution imaging with a C_S-probe-corrected scanning-transmission electron microscope in combination with X-ray diffractometry and Raman spectroscopy. The nanoplatelets (10 nm thick and from 50 nm to 200 nm wide) exhibit the Aurivillius-type layered-perovskite crystal structure that is characteristic of Bi₄Ti₃O₁₂, whereas the nanowires (from 15 nm to 35 nm wide and from several hundreds of nm to several μm long) exhibit an entirely new structure with an orthorhombic unit cell (a = 3.804(1) Å, b = 11.816(3) Å, and c = 9.704(1) Å). The nanowire structure is composed of two structural layers alternating along the orthorhombic c-direction: a structural layer composed of two parallel layers of Bi atoms that resembles the (Bi₂O₂)²⁺ layer of the Aurivillius structure, and a structural layer composed of two parallel layers of Ti atoms, where every sixth Ti is replaced with Bi. Observations of the ferroelectric domains with transmission electron and piezo-response force microscopy indicated the ferroelectric nature of both nanostructures. The nanowire structure is a metastable polymorph of the bismuth titanate stabilized at the nanoscale. With annealing at temperatures above 500 °C the nanowire structure topotactically transforms into the Aurivillius structure.