The increased CO2 emissions determined by the cement industry led to continuous and intensive research on the discovery of sustainable raw materials with cementitious properties. One such raw material category is agricultural waste. This study involved research on the effects of corn cob ash and sunflower stalk ash, respectively, on compressive strength measured after 28 days and 3 months, the flexural and splitting tensile strengths, the resistance to repeated freeze-thaw cycles, and on the resistance to chemical attack of hydrochloric acid of the concrete. A 2.5% and 5% replacement of the cement volume with corn cob ash (CCA) of A and B quality was applied, and with sunflower stalk ash (SSA) at A and B quality, respectively. The obtained results revealed that CCA and SSA decreased the compressive and tensile strength, but led to higher resistance of the concrete on repeated freeze-thaw cycles and to hydrochloric acid. The mixes with 2.5% SSA at A quality obtained the best results regarding splitting the tensile strength and resistance to repeated freeze-thaw cycles, the mixes with 2.5% SSA at B quality led to the highest resistance to hydrochloric acid, and those with 2.5% CCA at A quality led to the best values of compressive strength and flexural tensile strength.
Keywords: agro-waste; eco-friendly material; ecological concrete; sustainable building materials.