An activate pretreatment of zinc-containing metallurgical residues were proposed by adding CaO and introducing microwave heating approach into the CaO activation pretreatment process to realize the conversion of refractory ore phases into pre-treated ore phase. Thermodynamic characteristics analysis indicated that adding CaO can realize the conversion of refractory ore phases, with the same effect as the carbon additives. Thermal conductivity properties analysis denoted that the thermal conductivity properties of ZnS and ZnFe2O4 were relatively poor. Meanwhile, the thermal conductivity properties of the residues sample added with 25% CaO were significantly superior to the residues added with other CaO contents, with the maximum specific heat value of 1.348 J/g·K at 350 °C. Dielectric properties analysis highlighted that adding CaO with the dielectric constant properties significantly higher than that of other substances can enhance the microwave absorption capacity of zinc-containing residues. The decrease in dielectric loss and loss tangent value with the increase of temperature and the residues having large microwave penetration depth guaranteed to obtain better uniformity of microwave heating. Furthermore, adding 25% CaO promoted the microwave penetration depth of the residues sample increased in the range of 300-500 °C. This work can lay a theoretical research foundation for solving the key difficulty for efficient Zn recovery from complex zinc-containing metallurgical residues.
Keywords: calcium activation; dielectric properties; microwave heating; thermal conductivity; zinc-containing residues.