Composite materials composed of polylactide (PLA) and nano-hydroxyapatite (n-HA) have been recognized as excellent candidate material in bone repai The difference in hydrophilicity/hydrophobicity and poor interfacial compatibility between n-HA filler and PLA matrix leads to non-uniform dispersion of n-HA in PLA matrix and consequent poor reinforcement effect. In this study, an HA/PLA nanocomposite was designed based on the surface modification of n-HA with poly(D-lactide) (PDLA), which not only can improve the dispersion of n-HA in the poly(L-lactide) (PLLA) matrix but also could form a stereocomplex crystal with the matrix PLLA at the interface and ultimately lead to greatly enhanced mechanical performance The n-HA/PLA composites were characterized by means of scanning electron microscopy, Fourier transform infrared spectroscopy, X-Ray diffraction, thermal gravity analysis, differential scanning calorimetry, and a mechanical test; in vitro cytotoxicity of the composite material as well as its efficacy in inducing osteogenic differentiation of rat bone marrow stromal cells (rMSCs) were also evaluated. Compared with those of neat PLLA, the tensile strength, Young's modulus, interfacial shear strength, elongation at break and crystallinity of the composites increased by 34%, 53%, 26%, 70%, and 17%, respectively. The adhesion and proliferation as well as the osteogenic differentiation of rMSCs on HA/PLA composites were clearly evidenced. Therefore, the HA/PLA composites have great potential for bone repai.
Keywords: hydroxyapatite; mechanical property; nanocomposite; polylactide; stereocomplex.