Previously, we reported that amorphous poly(ethylene terephthalate) (PET) filled with irregular nodular aluminium (Al) particles gave simultaneous increases in tensile modulus, tensile strength, and impact resistance, which is unusual for materials. Here, we investigated the effect of the particle shape and size by using nano-platelet Al. The Al nano-platelets had a thickness higher than graphenes and clays, but lower than mica and talc, and due to their large widths, they had high aspect ratios. Due to the ductility of Al, the platelets maintained the high aspect ratio and did not snap during injection moulding. In addition to avoiding the usual drop in tensile strength and impact, the composites with nano Al platelets gave an unusually high flexural modulus (8 GPa), which was almost double that attained practically with talc, mica, and graphene. This was because of the high tendency of the Al nano platelets to become oriented during moulding. The Al-PET composite would be a more cost-and-performance effective combination for making conductive composites. The Al is a cheaper material than graphene, surface treatment for adhesion (to PET) is unnecessary, and dispersion issues, such as exfoliation and de-aggregation, are not a problem.
Keywords: aluminium nano-platelets; mechanical properties; metal–plastics; poly(ethylene terephthalate); reinforced polymer composite.