Excessive CO2 emissions have resulted in global warming and are a serious threat to the life of people, various strategies have been implemented to cut carbon emissions, and one of them is the use of a gas separation membrane to capture CO2 effectively. In this experiment, the butadiene-bridged polymethylsiloxane (BBPMS)/ethyl cellulose (EC)/ionic liquid (IL) ternary composite membranes were prepared by EC as a substrate, BBPMS, and IL as additives in tetrahydrofuran under high-speed stirring and coated on the membrane. The membrane structure was characterized by a Fourier transform infrared spectrometer and scanning electron microscope, and the membrane properties were tested by a membrane tensile strength tester, thermal weight loss analyzer, and gas permeability meter. The results show that the surface of the ternary composite membrane is dense and flat with a uniform distribution, and the membrane formation, heat resistance, and mechanical properties are good. The permeability coefficient of the ternary composite membrane for CO2 reached 1806.03 Barrer, which is 20.00 times higher than that of the EC/IL hybrid matrix membrane. The permeability coefficient of O2 reached 321.01 Barrer, which is 19.21 times higher than that of the EC/IL membrane. When the doping amount of BBPMS is 70-80%, the O2/N2 gas permeation separation of the BBPMS/EC/IL ternary composite membrane is close to the Robertson 2008 curve. It is always known that in the gas separation process the membrane material is the most crucial factor. The success of this experiment points to a new direction for the preparation of new membrane materials.
© 2022 The Authors. Published by American Chemical Society.