Reduced graphene oxide/cellulose nanocrystal composite films with high specific capacitance and tensile strength

Abstract

Due to the environmental degradation and energy depletion, the strategy for fabricating high-performance supercapacitor electrode materials based on graphene and nanocellulose has received great attention. Herein, an environmentally friendly reduced graphene oxide (RGO)/cellulose nanocrystal (CNC) composite conductive film was prepared using L-ascorbic acid (L-AA) as the reductant of graphene oxide (GO). Based on chemical structure analysis, L-AA was proved to be an effective reductant to remove oxygen containing groups of GO. Through microstructure observation, a unique stacking structure of CNC and RGO was observed, which could be largely attributed to the hydrogen bond interaction. Furthermore, the effect of CNC amount on the performance of RGO/CNC composite films was also systematically investigated. Particularly, the addition of CNC was found to exert a positive effect on the tensile strength, which might be mainly due to a mass of hydrogen bonds between the CNCs. Meanwhile, the RGO/CNC composite conductive film featured ideal electrical double-layer capacitive (EDLC) behavior, exhibiting a gravity specific capacitance of 222.5 F/g and tensile strength of 32.17 MPa at 20 wt% CNC content. Therefore, the RGO/CNC composite conductive films may hold great promise for environmentally friendly electrode materials of supercapacitors and flexible electrical devices.

Keywords: Cellulose nanocrystal; Composite conductive film; Hydrogen bond; Reduced graphene oxide; Specific capacitance; l-Ascorbic acid.