Objective: To evaluate the lubricating effect of hyaluronic acid (HA) on soft contact lenses (SCLs) measured using a pendulum-type friction tester.
Methods: We measured the coefficient of friction (CoF) of narafilcon A, delefilcon A, and etafilcon A with polyvinylpyrrolidone (PVP), daily disposable SCL material, using a modified pendulum-type friction tester. Sample SCLs were set on an acrylic plastic half-ball and placed into the polyethylene terephthalate hemisphere cup filled with 0.4 mL of test lubricants that included saline and 0.05%, 0.1%, 0.2%, 0.3%, 0.4%, and 0.5% (wt/vol) HA (molecular weight, 850 kDa). The viscosities of saline and HA were measured using an Ubbelohde viscometer.
Results: The CoF of the SCL under a low concentration (0.05%) of HA was the lowest and significantly lower than saline in narafilcon A and delefilcon A (P<0.05, Steel multiple comparison test). Under higher HA concentrations (0.3%, 0.4%, and 0.5%), the CoF was significantly higher than that of saline (P<0.01, Steel' multiple comparison test) in all three SCLs. There were no significant differences of CoF among three SCLs in saline and all concentrations of HA. The HA viscosities increased exponentially with the concentration (Y=1.2829e9.286X).
Conclusion: The viscosity of a high concentration of HA may increase the friction of SCLs, which may have a deleterious effect on the ocular surface.
Copyright © 2021 The Author(s). Published by Wolters Kluwer Health, Inc. on behalf of the Contact Lens Association of Opthalmologists.