The Corrosion Resistance and Mechanism of AT13/Fe-Based Amorphous Composite Coatings

Zhenhua Chu; Shikun Teng; Yuyun Zhou; Xingwei Zheng; Jingxiang Xu; Fang Wang; Baosen Zhang

doi:10.3390/mi13010056

The Corrosion Resistance and Mechanism of AT13/Fe-Based Amorphous Composite Coatings

Micromachines (Basel). 2021 Dec 29;13(1):56. doi: 10.3390/mi13010056.

Authors

Zhenhua Chu¹, Shikun Teng¹, Yuyun Zhou¹, Xingwei Zheng², Jingxiang Xu¹, Fang Wang¹, Baosen Zhang³

Affiliations

¹ Department of Mechanical Engineering, College of Engineering, Shanghai Ocean University, Shanghai 201306, China.
² College of Science, Donghua University, Shanghai 201620, China.
³ School of Materials Science and Technology, Nanjing Institute of Technology, Nanjing 211167, China.

Abstract

Due to high strength, high wear resistance and high corrosion resistance, the amorphous metallic glasses were investigated widely. In the present study, the corrosion resistance of amorphous coating and composite coatings with various proportions of AT13 (Al₂O₃-13 wt.% TiO₂) ceramic as additions in 3.5 wt.% NaCl solution were studied. The corrosion resistance was improved obviously as the addition of AT13, and when the content of AT13 was 15 wt.%, the composite coating had the lowest corrosion current density (1.75 × 10^-6 A cm^-2) and the highest corrosion potential (-411 mV), which was 5.14 × 10^-5 A cm^-2 and -580 mV for Fe-based metallic glassy coating, respectively. The corrosion mechanism was proposed according to the long-time immersion corrosion test.

Keywords: AT13; Fe-based amorphous coating; corrosion resistance; plasma spraying.

Abstract

Grants and funding