Photoluminescence enhancement study in a Bi-doped Cs2AgInCl6 double perovskite by pressure and temperature-dependent self-trapped exciton emission

Kashyap Dave; Wen-Tse Huang; Tadeusz Leśniewski; Agata Lazarowska; Dawid Jankowski; Sebastian Mahlik; Ru-Shi Liu

doi:10.1039/d1dt04047b

Photoluminescence enhancement study in a Bi-doped Cs₂AgInCl₆ double perovskite by pressure and temperature-dependent self-trapped exciton emission

Dalton Trans. 2022 Feb 1;51(5):2026-2032. doi: 10.1039/d1dt04047b.

Authors

Kashyap Dave^{1

2}, Wen-Tse Huang¹, Tadeusz Leśniewski³, Agata Lazarowska³, Dawid Jankowski³, Sebastian Mahlik³, Ru-Shi Liu^{1

4}

Affiliations

¹ Department of Chemistry, National Taiwan University, Taipei, Taiwan. rsliu@ntu.edu.tw.
² Taiwan International Graduate Program-Nano, Institute of Physics, Academia Sinica, Taipei, Taiwan.
³ Institute of Experimental Physics, Faculty of Mathematics, Physics and Informatics, University of Gdańsk, 80-308 Gdańsk, Poland.
⁴ Advanced Research Center of Green Materials Science and Technology, National Taiwan University, Taipei 106, Taiwan.

PMID: 35029610
DOI: 10.1039/d1dt04047b

Abstract

Here, we report a halide precursor acid precipitation method to synthesize Cs₂AgIn_1-xBi_xCl₆ (x = 0, 0.02, 0.04, 0.08, 0.16, 0.32, 0.64, and 1) microcrystals. Cs₂AgInCl₆ and Bi derivative double perovskites show broadband white light emission via self-trapped excitons (STEs) and have achieved the highest internal quantum efficiency of up to 52.4% at x = 0.08. Synchrotron X-ray diffraction confirmed the linear increase of lattice parameters and cell volume with Bi³⁺ substitution at In³⁺ sites. Absorbance, photocurrent excitation, and photoluminescence excitation spectra are used to observe possible transitions from the valence to the conduction band or free exciton (FE) states as well as transitions within local Bi³⁺ states. The broadband photoluminescence is quenched via a single nonradiative process with an activation energy ΔE = 1490 cm^-1 for Cs₂AgIn_0.92Bi_0.08Cl₆. Under normal conditions, we observed STE emission, but applying external pressure alters the electronic structure such that at elevated pressure, the only emission via the FE state is observed. We anticipate that structure, temperature and pressure-dependent photoluminescence studies will help the future use of a single-source lead-free double perovskite for white light-emitting diode applications.