This study aims to utilize the natural composition of brown seaweed by deriving alginate and cellulose concurrently from the stipe (stem-like) and blade (leaf-like) structures of the seaweed; further, this is followed by fibrillation for the direct and resource-efficient preparation of alginate/cellulose nanofiber (CNF) hybrid inks for three-dimensional (3D) printing of hydrogels. The efficiency of the fibrillation process was evaluated, and the obtained gels were further studied with regard to their rheological behavior. As a proof of concept, the inks were 3D printed into discs, followed by cross-linking with CaCl2 to form biomimetic hydrogels. It was shown that the nanofibrillation process from both seaweed structures is very energy-efficient, with an energy demand lower than 1.5 kW h/kg, and with CNF dimensions below 15 nm. The inks displayed excellent shear-thinning behavior and cytocompatibility and were successfully printed into 3D discs that, after cross-linking, exhibited an interconnected network structure with favorable mechanical properties, and a cell viability of 71%. The designed 3D biomimetic hydrogels offers an environmentally benign, cost-efficient, and biocompatible material platform with a favorable structure for the development of biomedical devices, such as 3D bio printing of soft tissues.
Keywords: 3D printing; alginate; biomedical application; biomimetic hydrogels; cellulose nanofibers; tissue engineering.