Mineral geopolymer binders can be an attractive and more sustainable alternative to traditional Portland cement materials for special applications. In geopolymer technology the precursor is a source of silicon and aluminium oxides, the second component is an alkaline solution. In the synthesis of geopolymer binders the most commonly used alkaline solution is a mixture of sodium or potassium water glass with sodium or potassium hydroxide or silicate solution with a low molar ratio, which is more convenient and much safer in use. In this paper, we present the influence of sodium or potassium silicate solution on the physical and mechanical properties of fly ash and ground granulated blast furnace slag-based geopolymer mortars. Mercury intrusion porosimetry and microstructural observation allowed for comparing the structure of materials with a different type of alkaline solution. The evolution of compressive and flexural tensile strength with time determined for composites using 10%, 30% and 50% slag contents (referring to fly ash mass) was analysed. The tests were performed after 3, 7, 14 and 28 days. It was observed that, as the amount of slag used increases in the precursor, the strength of the material grows. Mortars with the sodium alkaline solution were characterised by a higher strength at a young age. However, the values of strength 28 days were higher for geopolymers with potassium alkaline solution reaching 75 MPa in compression. Geopolymer mortar microstructure observation indicates a high matrix heterogeneity with numerous microcracks. Matrix defects may be caused by the rapid kinetics of the material binding reaction or shrinkage associated with the drying of the material.
Keywords: geopolymer; microstructure; sodium and potassium silicate solution; sustainability.