Fluoride and abrasives in toothpastes may cause corrosion and deterioration of the titanium used for implants and other prostheses. The purpose of this study was to investigate how the presence or absence and types of fluoride and abrasives affected the titanium surface texture. Brushing with toothpastes was performed on pure-titanium discs using an abrasive testing machine. Unprocessed titanium discs without brushing were used as control samples. Surface roughness, color, and gloss of titanium were measured and the differences compared with the control were analyzed. Additionally, titanium surfaces and abrasives in toothpastes were observed using a scanning electron microscope to compare the surface texture of each sample. Some toothpastes (abrasive+) significantly increased the difference in surface roughness, color, and gloss, compared with ultrapure water. Toothpaste (fluoride+/abrasive+) that had many polygonal abrasive particles led to the largest color differences and exhibited notable scratches and a larger number of contaminant- or corrosion-like black spots. In contrast, brushing with toothpaste without fluoride or abrasives (fluoride-/abrasive-) caused little change to the titanium surface. These results suggest that both fluoride and abrasives in toothpaste used for brushing may be factors that affect surface texture and corrosion resistance of titanium.
Keywords: abrasive; brushing; corrosion; fluoride; titanium surface; toothpaste.