Closed-cell rigid polyimide foams with excellent thermal stability and combined properties were prepared by thermal foaming of a reactive end-capped polyimide precursor powder in a closed mold. The precursor powder was obtained by thermal treatment of a polyester-amine salt (PEAS) solution derived from the reaction of the diethyl ester of 2,3,3',4'-biphenyl tetracarboxylic dianhydride (α-BPDE) with an aromatic diamine mixture of p-phenylenediamine (PDA) and 2-(4-aminophenyl)-5-aminobenzimidazole (BIA) in the presence of an end-capping agent (mono-ethyl ester of nadic acid anhydride, NE) in an aliphatic alcohol. The effect of polymer mainchain structures on the foaming processability and combined properties of the closed-cell rigid polyimide foams were systematically investigated. The polyimide foams (100-300 kg/m3) with closed-cell rates of 91-95% show an outstanding thermal stability with an initial thermal decomposition temperature of ≥490 °C and a glass transition temperature of 395 °C. Polyimide foams with density of 250 kg/m3 exhibited compression creep deformation as low as 1.6% after thermal aging at 320 °C/0.4 MPa for 2 h.
Keywords: benzimidazole; high temperature; polyimide foam; rigid closed-cell foam.