In this study, polymer blends with a mechanical property balance based on poly(lactic acid) (PLA), stiff polymer, and elongated polymer were developed. First, the binary blends PLA-elongated polymer [ethyl vinyl acetate (EVA) or polyethylene], or PLA-stiff polymer [polystyrene or poly(styrene-co-methyl methacrylate) (SMMA)] blends were studied using dynamic mechanic analysis (DMA) and analyzed using Minitab statistical software to determine the factors influencing the elongation or stiffness of the blends. Then, ternary blends such as elongation-poly(lactic acid)-stiff, were made from the binary blends that presented optimal performance. In addition, three blends [EVA-PLA-SMMA (EPS)] were elaborated by studying the mixing time (5, 15, and 15 min) and the added time of the SMMA (0, 0, and 10 min). Specifically, the mixing time for EPS 1, EPS 2, and EPS 3 is 5 min, 15 min, and 15 min (first EVA + PLA for 10 min, plus 5 min PLA-EVA and SMMA), respectively. Mechanical, thermal, rheological, and morphological properties of the blends were studied. According to DMA, the results show an increase in elongation at break (εb) and do not decrease the elastic module of poly(lactic acid). Nevertheless, EPS 3 excels in all properties, with an εb of 67% and modulus of elasticity similar to PLA. SMMA has a significant role as a compatibilizing agent and improves PLA processability.
Keywords: EVA; PLA; SMMA; elongated polymer; mechanical properties balance; polymer blends; stiff polymer.