Aluminum dross is a well-known industrial waste generated in the aluminium industry, and its recycling and reuse is still a worldwide issue. Herein, aluminum dross waste (ADW) was recycled to progressively replace the aggregate fraction of clay at 70, 75, 80, 85, and 90 wt% for the fabrication of Al2O3-SiO2-rich porous castable refractories. Their physical properties and mechanical behavior were assessed by the measurement of linear shrinkage rate, bulk density, apparent porosity, cold crushing strength, and thermal conductivity. The microstructure and phase evolutions were analyzed via scanning electron microscopy (SEM) and X-ray diffraction (XRD). The incorporation of 85 wt% of ADW allowed the development of a waste-containing conventional refractory castable with improved properties as compared to those of the other samples. The sustainable refractory castable exhibited decent thermal conductivity and physical and mechanical characteristics, and is suitable for application as reheating furnace lining. It is a "green" practice to partially replace the traditional raw materials with industrial waste in the manufacture of conventional refractory castables and provides environmental and economic benefits.
Keywords: aluminum dross waste; castable; mechanical properties; thermal conductivity.