Background: Linen dressings were invented a few years ago but are still being worked on.
Methods: The obtained fabrics from the traditional variety of flax (Nike), two transgenic types of flax (M50 and B14) and the combination of these two flax fibers (M50 + B14) were tested in direct contact in cell cultures. Cell viability tests were performed, and the proliferation potential of cells on Balb3T3 and NHEK cell lines was checked using the Sulforhodamine-B (SRB) test. Moreover, the effect of new linen fabrics on apoptosis of THP-1 cells, as well as on the cell cycle of NHEK, HMCEV and THP-1, cells after 24 h of incubation was assessed.
Results: All tested linen fabrics did not raise the number of necrotic cells. The tested fabrics caused a statistically significant decrease in the total protein content in skin cancer (except for 0.5 cm of Nike-type fabrics). The smallest cells in the apoptotic phase were in cultures treated with M50 fiber on an area of 0.5 cm. After 48 h of incubation of HEMVEC, NHEK and THP-1 cells with the tested fabrics, the growth of S-phase cells was noticed in all cases. At the same time, the greatest increase was observed with the use of B14 fabric. Necrosis is not statistically significant.
Conclusions: All the obtained flax fibers in the form of flax dressings did not lose their wound-healing properties under the influence of the technological process. New dressings made of genetically modified flax are a chance to increase the effectiveness of treatment of difficult healing wounds.
Keywords: flax fabrics; healing wound; linen dressings.