Pd + Zr co-doped aluminide coatings were deposited on the CMSX-4 nickel superalloy, widely used in the aircraft industry, in order to investigate their microstructure and improvement of oxidation resistance. Palladium was deposited by the electrochemical method, whereas zirconium and aluminum by the chemical vapor deposition (CVD) method. Coatings consist of two zones: the additive and the interdiffusion one. The additive zone contains β-(Ni,Pd)Al phase with some zirconium-rich precipitates close to the coating's surface, whereas the interdiffusion zone consists of the same β-(Ni,Pd)Al phase with inclusions of refractory elements that diffused from the substrate, so called topologically closed-packed phases. Palladium dissolves in the β-NiAl phase and β-(Ni,Pd)Al phase is being formed. Pd + Zr co-doping improved the oxidation resistance of analysed coatings better than Pd mono-doping. Mechanisms responsible for this phenomenon and the synergistic effect of palladium and zirconium are discussed.
Keywords: aluminide coatings; co-doping; nickel superalloys; oxidation resistance.