The exoskeleton of the pinching side of claws with denticles and of the outer side without them on the coconut crab, Birgus latro, which is a rare organism, were studied using a materials science approach. The mechanical resistance of three claws of different sizes was investigated along the exoskeleton thickness from the outer surface to the inner surface, and the results were compared, including the contribution of the microstructure and chemical compositions. Mechanical properties, hardness (H) and stiffness (Er), were probed through nanoindentation tests. The results showed the H, Er, microstructures, and chemical components of the exocuticle and endocuticle layers were almost the same, in a BW range of 300 g to 1650 g. At the same time, the H and Er near the surface of the denticles of a small coconut crab of 300 g were lower than those of other large coconut crabs. The microstructure of the denticles was clearly different from that of the exocuticle, but the maximum mechanical properties near their surface indicated almost the same values, Hmax = 4 GPa and Er(max) = 70 GPa, regardless of being on the pinching side or the outer side. A denticle can be regarded as a bulge of the cuticle without phosphorus and with high magnesium. The results provided novel information that expanded our knowledge about the claw microstructure of coconut crabs with different body sizes, and may be used in further studies.
Keywords: biomineralization; coconut crab; cuticle; denticle; microstructure; nanoindentation.