Chemically ordered intermetallic nanoparticles are promising candidates for energy-related applications such as electrocatalysis. However, the synthesis of intermetallics generally requires long annealing (several hours) to achieve the ordered structure, which causes nanoparticles agglomeration and diminished performance, particularly for catalysis. Herein, we demonstrate a new rapid Joule heating approach that can synthesize highly ordered and well-dispersed intermetallic nanoparticles. As a proof-of-concept, we synthesized fully ordered Pd3Pb intermetallic nanoparticles that feature small size distribution (∼6 nm). Computational analysis of the L12 Pd3Pb material suggests that this rapid atomic ordering transformation can be attributed to a vacancy-mediated diffusion mechanism. Moreover, the nanoparticles demonstrate excellent electrocatalytic activity and exceptional stability for the oxygen reduction reaction (ORR), retaining >95% of the current density over 10 h of chronoamperometry test with negligible structural and compositional changes. This study demonstrates a new strategy of providing a new direction for intermetallic synthesis and catalyst discovery.
Keywords: atomic ordering; intermetallic; nanoparticle synthesis; oxygen reduction reaction.