In this paper, we have examined the influence of electroplated gold thickness on the thermal and electro-optical properties of mid-IR AlInAs/InGaAs, InP QCLs. The experimental results show a significant reduction of the temperature of QCL active region (AR) with increasing gold layer thickness. For QCLs with 5.0 μm gold thickness, we observed a 50% reduction of the active region temperature. An improvement of key electro-optical parameters, that is, threshold current density and maximum emitted power for structures with thick gold, was observed. The results of micro-Raman characterization show that the electroplated gold layer introduces only moderate compressive strain in top InP cladding, which is well below the critical value for the creation of misfit dislocations.
Keywords: Raman spectroscopy; gold electroplating; quantum cascade lasers; thermoreflectance.