In this paper, hot-dip aluminizing of ferrite nodular cast iron was carried out after treating liquid aluminum with different electrical pulse parameters. Compared with that of conventional hot-dip aluminizing, the coating structure of the treated sample did not change, the surface was smooth and continuous, and the solidification structure was more uniform. When high voltage and large capacitance were used to treat the liquid aluminum, the thickness and compactness of the coating surface layer increased. The thickness of the alloy layer decreased, and, the compactness and the micro hardness increased, so the electric pulse had a certain inhibition on the formation of the alloy layer. The growth kinetics of the alloy layer showed that the rate-time index decreased from 0.60 for the conventional sample to 0.38 for the electric pulse treated sample. The growth of the alloy layer was controlled by diffusion and interface reaction, but only by diffusion. The AC impedance and polarization curves of the coating showed that the corrosion resistance of hot-dip coating on nodular cast iron was improved by electric pulse treatment.
Keywords: corrosion resistance; ductile iron; dynamics; electric pulse; hot-dip aluminizing.