Bacterial sample preparation is crucial for its observation by scanning electron microscopy (SEM). However, the current polylysine (PLL) method leads to bacterial morphological changes. To overcome this problem, we employed chitosan (CS) to coat coverslips to prepare bacteria for SEM and compared it with the PLL method. Coverslips coated with 0.025% (w/v) CS showed satisfactory bacterial binding ability. Within 30 min of binding time, the number of bacteria on CS-coated and PLL-coated coverslips exhibited no differences. Four bacteria strains were employed to compare the differences in SEM images between the two methods. Most of the bacteria showed irregular surface or sticky substances after settling on PLL-coated coverslips, while bacteria with clear surface texture were observed on CS-coated coverslips. Transmission electron microscopy (TEM) images showed deformed bacterial envelope on PLL-coated coverslips; meanwhile, similar intact envelope was observed from the bacteria on CS-coated coverslips and the bacteria without any treatment. The TEM results verified the morphological differences of SEM between the two methods. Except for morphology, the length of the rod-shaped bacteria was longer on CS-coated coverslips than that on PLL-coated coverslips, less shrinkage of the sample was observed, and CS could preserve the length of the rod-shaped bacteria better than PLL in its preparation for SEM. It is demonstrated that the low-cost CS could be utilized in bacterial preparation for SEM to acquire preferable images. Bacterial suspension with optical density at 600 nm of about 0.5, deposited on 0.025% CS-coated coverslips for 30 min, and followed by routine fixation, dehydration, and drying are optimal parameters.
Keywords: SEM; TEM; bacteria; chitosan; polylysine.
© 2021 Wiley Periodicals LLC.