High fluorescent graphene quantum dots (GQDs) are promising in bioimaging and optoelectronics. In this paper, bright blue fluorescent N-doped GQDs were synthesized using a ultrasonic-assisted hydrothermal method. The morphology, structure, surface chemistry, optical properties, and stability subject to photo-bleaching, temperature, pH and preservation period for the N-GQDs were investigated in detail using various microscopy and spectroscopy techniques. The results showed that the N-GQDs possessed an average size of 2.65 nm, 3.57% N doping, and up to 54% quantum yield (QY). The photoluminescence (PL) spectra of the N-GQDs are excitation dependent when excited in the range of 300-370 nm and excitation independent in the range of 380-500 nm for the core and surface states emission. The N-GQDs showed excellent photo-bleaching resistance and superior photo-stability. At room temperature and in the pH range of 3-8, the fluorescence of the N-GQDs was almost invariable. The N-GQDs can be stably preserved for at least 40 days. The average decay lifetime of the N-GQDs was 2.653 ns, and the radiative and nonradiative decay rate constants were calculated to be 2.04 × 108 s-1 and 1.73 × 108 s-1, respectively. The PL mechanism was qualitatively explained. The N-GQDs was used for cell imaging, and it showed good results, implying great potential applications for bioimaging or biomarking.
Keywords: cell imaging; nitrogen doped graphene quantum dots; optical properties; photo-stability; ultrasonic-assisted hydrothermal.