A poly(l-lactic acid)/nanohydroxyapatite (PLLA/nHA) scaffold works as a bioactive, osteoconductive scaffold for bone-tissue engineering, but its low degradation rate limits embedded HA in PLLA to efficiently interact with body fluids. In this work, nano-hydroxyapatite (nHA) was added in lower filler loadings (1, 5, 10, and 20 wt%) in a poly(l-lactic acid)/cyclo olefin copolymer10 wt% (PLLA/COC10) blend to obtain novel poly(l-lactic acid)/cyclo olefin copolymer/nanohydroxyapatite (PLLA/COC10-nHA) scaffolds for bone-tissue regeneration and repair. Furthermore, the structure-activity relationship of PLLA/COC10-nHA (ternary system) nanocomposites in comparison with PLLA/nHA (binary system) nanocomposites was systematically studied. Nanocomposites were evaluated for structural (morphology, crystallization), thermomechanical properties, antibacterial potential, and cytocompatibility for bone-tissue engineering applications. Scanning electron microscope images revealed that PLLA/COC10-nHA had uniform morphology and dispersion of nanoparticles up to 10% of HA, and the overall nHA dispersion in matrix was better in PLLA/COC10-nHA as compared to PLLA/nHA. Fourier transformation infrared spectroscopy (FTIR), powder X-ray diffraction (XRD), and differential scanning calorimetry (DSC) studies confirmed miscibility and transformation of the α-crystal form of PLLA to the ά-crystal form by the addition of nHA in all nanocomposites. The degree of crystallinity (%) in the case of PLLA/COC10-nHA 10 wt% was 114% higher than pure PLLA/COC10 and 128% higher than pristine PLLA, indicating COC and nHA are acting as nucleating agents in the PLLA/COC10-nHA nanocomposites, causing an increase in the degree of crystallinity (%). Moreover, PLLA/COC10-nHA exhibited 140 to 240% (1-20 wt% HA) enhanced mechanical properties in terms of ductility as compared to PLLA/nHA. Antibacterial activity results showed that 10 wt% HA in PLLA/COC10-nHA showed substantial activity against P. aeruginosa, S. aureus, and L. monocytogenes. In vitro cytocompatibility of PLLA/COC10 and PLLA nanocomposites with nHA osteoprogenitor cells (MC3T3-E1) and bone mesenchymal stem cells (BMSC) was evaluated. Both cell lines showed two- to three-fold enhancement in cell viability and 10- to 30-fold in proliferation upon culture on PLLA/COC10-nHA as compared to PLLA/nHA composites. It was observed that the ternary system PLLA/COC10-nHA had good dispersion and interfacial interaction resulting in improved thermomechanical and enhanced osteoconductive properties as compared to PLLA/nHA.
Keywords: bone-tissue engineering; cyclo olefin copolymer; cytotoxicity; hydroxyapatite; mechanical properties; poly(l-lactic acid).