The flow diverting stent (FDS) has become a promising endovascular device for the treatment of aneurysms. This research presents a novel biodegradable and non-braided Polycaprolactone (PCL) FDS. The PCL FDS was designed and developed using an in-house fabrication unit and coated on two ends with BaSO4 for angiographic visibility. The mechanical flexibility and quality of FDS surfaces were examined with the UniVert testing machine, scanning electron microscope (SEM), and 3D profilometer. Human umbilical vein endothelial cell (HUVEC) adhesion, proliferation, and cell morphology studies on PCL FDS were performed. The cytotoxicity and NO production by HUVECs with PCL FDS were also conducted. The longitudinal tensile, radial, and bending flexibility were found to be 1.20 ± 0.19 N/mm, 0.56 ± 0.11 N/mm, and 0.34 ± 0.03 N/mm, respectively. The FDS was returned to the original shape and diameter after repeated compression and bending without compromising mechanical integrity. Results also showed that the proliferation and adhesion of HUVECs on the FDS surface increased over time compared to control without FDS. Lactate dehydrogenase (LDH) release and NO production showed that PCL FDS were non-toxic and satisfactory. Cell morphology studies showed that HUVECs were elongated to cover the FD surface and developed an endothelial monolayer. This study is a step forward toward the development and clinical use of biodegradable flow diverting stents for endovascular treatment of the aneurysm.
Keywords: Polycaprolactone (PCL) flow diverters; aneurysms; biodegradable; endovascular treatment; flow diverting stents (FDS).