Multilayer Films Based on Poly(lactic acid)/Gelatin Supplemented with Cellulose Nanocrystals and Antioxidant Extract from Almond Shell By-Product and Its Application on Hass Avocado Preservation

Arantzazu Valdés; Carmen Martínez; Mari Carmen Garrigos; Alfonso Jimenez

doi:10.3390/polym13213615

Multilayer Films Based on Poly(lactic acid)/Gelatin Supplemented with Cellulose Nanocrystals and Antioxidant Extract from Almond Shell By-Product and Its Application on Hass Avocado Preservation

Polymers (Basel). 2021 Oct 20;13(21):3615. doi: 10.3390/polym13213615.

Authors

Arantzazu Valdés¹, Carmen Martínez¹, Mari Carmen Garrigos¹, Alfonso Jimenez¹

Affiliation

¹ Analytical Chemistry, Nutrition & Food Sciences Department, University of Alicante, P.O. Box 99, 03080 Alcante, Spain.

Abstract

In this work, poly(lactic acid) (PLA)/gelatin/PLA multilayer films supplemented with cellulose nanocrystals and antioxidant extract from almond shell (AS) by-products were developed by solvent casting technique for active food packaging. The almond shell antioxidant extract (ASE) was obtained by microwave-assisted extraction, while cellulose nanocrystals (CNCs) were extracted from AS by a sequential process of alkalization, acetylation and acid hydrolysis. Four formulations were obtained by adding 0 (control), 6 wt.% of ASE (FG/ASE), 4.5 wt.% of CNCs (FG/CNC) and 6 wt.% + 4.5 wt.% of ASE + CNCs, respectively, (FG/ASE + CNC) into fish gelatin (FG). PLA/FG/PLA multilayer films were prepared by stacking two outer PLA layers into a middle FG film. A surface modification of PLA by air atmospheric plasma treatment was optimized before multilayer development to improve PLA adhesion. Complete characterization of the multilayers underlined the FG/ASE + CNC formulation as a promising active reinforced packaging system for food preservation, with low values of transparency, lightness and whiteness index. A good adhesion and homogeneity of the multilayer system was obtained by SEM, and they also demonstrated low oxygen permeability (40.87 ± 5.20 cm³ mm m^-2 day) and solubility (39.19 ± 0.16%) values, while mechanical properties were comparable with commercial plastic films. The developed multilayer films were applied to Hass avocado preservation. The initial degradation temperature (T_ini), DSC parameters and in vitro antioxidant capacity of the films were in accordance with the low peroxide and anisidine values obtained from avocado pulp after packaging for 14 days at 4 °C. The developed PLA/FG/PLA films supplemented with 6 wt.% ASE+ 4.5 wt.% CNCs may be potential bioactive packaging systems for fat food preservation.

Keywords: active packaging; almond shell by-product; antioxidant activity; avocado preservation; corona treatment; fish gelatin; multilayer film; poly(lactic acid); reinforcing agent.