In the current work, we present the facile one-pot synthesis of 0.0, 0.5, 1.0, 2.0 and 3.0 wt% of Ni doped ZnO nanoparticles (Ni:ZnO NPs) through combustion route at 550 °C. Structural and vibrational studies approve the synthesis of monophasic hexagonal Ni:ZnO NPs. The crystallite size was calculated to be in the range of 36-60 nm for pure and doped samples. The composition of all elements in the final product along with their homogeneity, was approved through EDX/FESEM e-mapping analysis. The morphology and phase confirmation of the prepared samples was investigated through FESEM and TEM/HRTEM analyses. TEM/HRTEM study shows that the size of grains is within the range of 100 nm and grown along the c-axis as the lattice spacing is found ∼2.6005 Å. Diffused reflectance study was used to estimate the energy gap for all samples and found to reduce from 3.287 eV for pure to 3.258 eV for 3.0 wt% Ni doping. From an applications point of view, the photocatalytic performance of Ni:ZnO NPs was studied, and with 3.0 wt% of Ni doping in ZnO the degradation of methylene blue (MB) and tetracycline (TCN) pollutants were found to be remarkably improved.
Keywords: Combustion; Hazardous dye degradation; Ni:ZnO NPs; Optical properties; Photocatalysis.
Copyright © 2021 Elsevier Ltd. All rights reserved.