Calcium silicate-based cements are biocompatible materials for vital pulp therapy. However, they discolour the tooth tissue, which is important for the aesthetics of the anterior teeth. The aim of this study was to investigate the effect of calcium silicate-based cements on tooth discolouration. The study included 70 extracted bovine incisors. The crown of the tooth was cut off from the root, 2 mm below the cement-enamel junction. The pulp tissue was removed via a cervical cut with a barbed broach. The teeth were randomly divided into five experimental, one positive, and one negative control groups. The evaluated materials included Biodentine, Ortho MTA, Retro MTA, MTA Plus, MTA Repair HP, and in the positive group, ProRoot MTA. A VITA Easyshade Compact 5.0 spectrophotometer was used before the application, after 1 week, 1 month, 3 months, and 6 months. The significance levels were set at p < 0.05. All materials significantly changed the teeth colour (p < 0.05). However, Ortho MTA, ProRoot MTA, MTA Plus, and Biodentine (ΔE > 6) caused maximum colour change after 6 months. While the ProRoot MTA, Ortho MTA, and MTA Plus caused grey discolouration, Biodentine darkened the shade of the base colour. Thus, Retro MTA and MTA Repair HP can be safely used in the aesthetic dentition zone. According to these clinical results, the possibility of using Biodentine, due to its lack of gray discoloration, can be considered.
Keywords: biomaterials; calcium silicate-based cements; endodontics; staining potential; tooth discolouration.