Ionogels have been extensively studied as ideal flexible and stretchable materials by virtue of the unique properties of ionic liquids, such as non-volatility, non-flammability, and negligible vapor pressure. However, the generally low ionic conductivity of the current ionogels limits their applications in the market of highly conductive, flexible, and stretchable electrical devices. Here, the fabrication of highly electrically conductive ionogels is reported by combining composite liquids consisting of 1-ethyl-3-methylimidazolium dicyanamide ([EMIM][DCA]) and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) with flexible negative-charged poly(2-acrylamido-2-methyl-1-propanesulfonic acid) (PAMPS) hydrogel. The generated composite film exhibits high electrical conductivity up to about 38 S cm-1 with the maximum tensile strain of 45% and fracture stress of 27 kPa. In addition, it is demonstrated that the composite film can maintain conductivity in a high level under different mechanical deformations, and can also be used as flexible sensors in a wide temperature range from -58 to 120 ℃. It is believed that the designed composite film would expand the applications of flexible conductive materials where both high conductivity and robust mechanical flexibility are required.
Keywords: composite liquids; conductive films; flexible films; ionogels; poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate).
© 2021 Wiley-VCH GmbH.