Polyketones (PKs) having strong hydrogen bonding properties and a chain extender are used as additives in the melt processing of nylon 6 (PA6). Their effect on the chain structure and properties of PA6 is studied to enhance the processability of PA6 in melt processing. The addition of the chain extender to PA6 increases the melt viscosity by forming branches on the backbone. The addition of PKs results in an additional increase in viscosity through the hydrogen bonding between N-H of PA6 and C=O of PK. The change in the N-H bond FT-IR peak of PA6 and the swelling data of the PA6/PK blend containing a chain extender, styrene maleic anhydride copolymer (ADR), suggest that incorporation of chain extender and PK in the melt processing of PA6 results in physical crosslinks through hydrogen bonding between the branched PA6 formed by the addition of chain extender and PK chains. This change in the chain structure of PA6 not only increases the melt strength of PA6 but also increases randomness resulting in decreased crystallinity.
Keywords: chain branching; chain crosslinking; chain extender; hydrogen bonding; melt viscosity; nylon 6; polyketone.