Synthesis of Pd3 Sn and PdCuSn Nanorods with L12 Phase for Highly Efficient Electrocatalytic Ethanol Oxidation

Abstract

The crystal phase of nanomaterials is one of the key parameters determining their physicochemical properties and performance in various applications. However, it still remains a great challenge to synthesize nanomaterials with different crystal phases while maintaining the same composition, size, and morphology. Here, a facile, one-pot, wet-chemical method is reported to synthesize Pd₃ Sn nanorods with comparable size and morphology but different crystal phases, that is, an ordered intermetallic and a disordered alloy with L1₂ and face-centered cubic (fcc) phases, respectively. The crystal phase of the as-synthesized Pd₃ Sn nanorods is easily tuned by altering the types of tin precursors and solvents. Moreover, the approach can also be used to synthesize ternary PdCuSn nanorods with the L1₂ crystal phase. When used as electrocatalysts, the L1₂ Pd₃ Sn nanorods exhibit superior electrocatalytic performance toward the ethanol oxidation reaction (EOR) compared to their fcc counterpart. Impressively, compared to the L1₂ Pd₃ Sn nanorods, the ternary L1₂ PdCuSn nanorods exhibit more enhanced electrocatalytic performance toward the EOR, yielding a high mass current density up to 6.22 A mg_Pd ^-1 , which is superior to the commercial Pd/C catalyst and among the best reported Pd-based EOR electrocatalysts.

Keywords: L1 2 phase; Pd 3Sn; PdCuSn; ethanol oxidation reaction; nanorods.