Recently, appreciable ionic conduction has been frequently observed in multifunctional semiconductors, pointing out an unconventional way to develop electrolytes for solid oxide fuel cells (SOFCs). Among them, ZnO and Li-doped ZnO (LZO) have shown great potential. In this study, to further improve the electrolyte capability of LZO, a typical ionic conductor Sm0.2Ce0.8O1.9 (SDC) is introduced to form semiconductor-ionic composites with LZO. The designed LZO-SDC composites with various mass ratios are successfully demonstrated in SOFCs at low operating temperatures, exhibiting a peak power density of 713 mW cm-2 and high open circuit voltages (OCVs) of 1.04 V at 550 °C by the best-performing sample 5LZO-5SDC, which is superior to that of simplex LZO electrolyte SOFC. Our electrochemical and electrical analysis reveals that the composite samples have attained enhanced ionic conduction as compared to pure LZO and SDC, reaching a remarkable ionic conductivity of 0.16 S cm-1 at 550 °C, and shows hybrid H+/O2- conducting capability with predominant H+ conduction. Further investigation in terms of interface inspection manifests that oxygen vacancies are enriched at the hetero-interface between LZO and SDC, which gives rise to the high ionic conductivity of 5LZO-5SDC. Our study thus suggests the tremendous potentials of semiconductor ionic materials and indicates an effective way to develop fast ionic transport in electrolytes for low-temperature SOFCs.
Keywords: Li-doped ZnO; SOFCs; composite electrolyte; high ionic conductivity; interfacial conduction.