Mg-Al-Ca-Mn alloys with Ca/Al ≥ 1 of AX33, AX44, and AX55 were prepared by combining three processes of water-cooling semi-continuous cast, homogenization heat treatment, and hot extrusion. The as-fabricated alloys translated into composites consisting of α-Mg solid solution + granular Al2Ca. These alloys exhibited some favourable properties such as a tensile strength of 324~350 MPa at room temperature and 187~210 MPa at elevated temperature of 423 K, an ignition temperature of 1292~1344 K, and so on. Variation trend between performance and content of Al and Ca is given in this paper. The result indicated that the emerged second-phase Al2Ca in the alloys was beneficial to the improvement in mechanical properties, heat resistance, flame retardation, and corrosion resistance.
Keywords: Mg alloys; high Ca/Al ratio; hot extrusion; mechanical properties.