Duplex stainless steels are being used on applications that require high corrosion resistance and excellent mechanical properties, such as the naval and oil-gas exploration industry. The components employed in these industries are usually obtained by machining; however, these alloys have low machinability when compared to conventional stainless steels, usually requiring the employment of tool coatings. In the present work, a comparative study of TiAlSiN coating performance obtained by these two techniques in the milling of duplex stainless-steel alloy LDX 2101 was carried out. These coatings were obtained by the conventional direct current magnetron sputtering (dc MS) and the novel high power impulse magnetron sputtering (HiPIMS). The coatings were analyzed and characterized, determining mechanical properties for both coatings, registering slightly higher mechanical properties for the HiPIMS-obtained coating. Machining tests were performed with varying cutting length and feed-rate, while maintaining constant values for axial and radial depth of cut and cutting speed. The surface roughness of the material after machining was assessed, as well as the wear sustained by each of the tool types, identifying the wear mechanisms and behavior of these tools, as well as registering the flank wear values presented for each of the tested tools. The HiPIMS-obtained coating exhibited a very similar behavior when compared to the other, producing similar surface roughness quality. However, the HiPIMS coating exhibited less wear for higher cutting lengths, proving to be a better choice in this case, especially regarding tool life.
Keywords: HiPIMS; TiAlSiN; abrasion; adhesion; dc MS; duplex stainless-steel; milling; surface roughness; wear mechanisms; wear performance.