This study evaluated the effect of different protocols for Ca(OH)2 removal on the bond strength (BS) of epoxy resin-based sealer in long oval root canals. Forty-eight mandibular incisors with long oval root canals were selected by CBCT. Biomechanical preparation was performed, the samples were filled with Ca(OH)2 paste and distributed in four groups (n = 12): G-without Ca(OH)2 paste (C); G2-syringe/needle (SN); G3-SN + XP-Endo® Finisher (XPF); G4-SN + passive ultrasonic irrigation (PUI). After 7 days, Ca(OH)2 was removed and teeth were filled using AHPlus and guttapercha. In four samples from each group, the sealer was manipulated with 0.1% rhodamine to assess sealer penetration by fluorescent laser confocal microscopy (FLCM). Samples were sectioned in slices for BS, scanning electron microscopy, and FLCM analysis. The BS data were analyzed by ANOVA and Tukey tests (α = 0.05). The lowest BS values were found for the SN group (12.89 ± 4.36) compared to C (35.55 ± 10.05), while PUI group presented intermediate values (28.57 ± 9.35) and the XPF group (31.34 ± 9.8) showed values that were sometimes similar to C group and sometimes similar to PUI group (p > .05). The analysis of the adhesive interface showed evident gaps, with the presence of residues between the dentin and the filling material for the SN group, and for C, XPF and PUI groups juxtaposed adhesive interface. FLCM images showed sealer penetration in the dentinal tubules along the entire perimeter for C, XPF, and PUI groups. Ca(OH)2 removal with XPF and PUI from long oval root canals resulted in higher bond strength values compared to SN, besides better sealer penetration on dentinal tubules and juxtaposed adhesive interface.
Keywords: bond strength; calcium hydroxide; intracanal medication.
© 2021 Wiley Periodicals LLC.