The main objective of this study focuses on designing and testing body protection systems using advanced materials based on aramid fibers, for high impact speeds of up to 420 ± 10 m/s. Ballistic applications of aramid fiber-based composites mostly include soft body armors. The investigation of the failure mechanisms identifies issues of protective fabrics, major challenges and technological problems for efficient development of these systems. The authors present an investigation on the failure processes and destructive stages of a ballistic package made of successive layers of LFT SB1plus, a trade name for a multiaxial fabric by Twaron Laminated Fabric Technology (LFT), taking into account the particular test conditions from NIJ Standard-0101.06 Ballistic Resistance of Body Armor. The main parameter of interest was the backface signature (BFS), but also details of projectile arrest and SEM investigation could offer arguments for using this material for individual protection. For the reported tests, the maximum and minimum values for BFS were 12 mm and 24 mm, the mean value being 18.66 mm and the standard deviation being 3.8 mm.
Keywords: aramid fiber; ballistic test; failure mechanism.