The main goal of this work was the evaluation of the interfacial strength of the carbon fibres/aluminium matrix interface dependently on the utilised composite fabrication method, namely high pressure die casting and gas pressure infiltration. In addition, the influence of a Ni-P coating on the C-fibres was investigated. The proposed measurements of the interfacial strength were carried out by means of the "push-out" method. The interfacial strength of the samples fabricated using the high-pressure infiltration method average between 19.03 MPa and 45.34 MPa.
Keywords: fibre/matrix bond; interface/interphase; liquid metal infiltration; metal-matrix composites (MMC).