Preparation and application of polyethylene glycol triazine derivatives as a chrome-free tanning agent for wet-white leather manufacturing

Abstract

Leather manufacturing is the process of transforming animal skin into high value-added commodity. As a crucial step in the leather producing process, conventional chrome tanning could lead to discharge of chromium contaminant due to the low efficiency of chromium uptake. In this paper, a series of polyethylene glycol triazine derivatives' tanning agent (PT) with different molecule weight was synthesized with one-step method and applied in the main tanning of hide. The chemical structure of the PT was detected by FT-IR and ¹H-NMR. The application experimental results indicated that after 16% of PT tanning at pH of 6, the wet-white was endowed with shrinkage temperature over 80°C and thickening rate over 108%. The experimental results indicated that the PT tanning leather not only have a better physical and mechanical properties than commercial triazine derivatives tanning agent, but also the leather is endowed with the effects of outstanding thermal properties. Considering that the pickling process became unnecessary, a large number of neutral salts could be avoided, the chromium load in spent liquor decreased from 1288 mg/L to 0, and the total dissolved chlorine in spent liquor decreased from 15,360 to 9581 mg/L; no toxic and harmful substances such as chromium and aldehyde are introduced into the tanning process. Compared with the leather tanned with commercial triazine derivatives' tanning agent, the leather tanned with PT showed a similar overall tanning properties and better environmental friendliness, which makes PT matches the integral requirements of the modern sustainable leather industry.

Keywords: Chrome-free tanning; Cyanuric chloride; Leather manufacture; Polyethylene glycol.