The purpose of this paper is to study the effect of nano-bismuth ferrite (BiFeO3) on the electrical properties of low-density polyethylene (LDPE) under magnetic-field treatment at different temperatures. BiFeO3/LDPE nanocomposites with 2% mass fraction were prepared by the melt-blending method, and their electrical properties were studied. The results showed that compared with LDPE alone, nanocomposites increased the crystal concentration of LDPE and the spherulites of LDPE. Filamentous flake aggregates could be observed. The spherulite change was more obvious under high-temperature magnetization. An agglomerate phenomenon appeared in the composite, and the particle distribution was clear. Under high-temperature magnetization, BiFeO3 particles were increased and showed a certain order, but the change for room-temperature magnetization was not obvious. The addition of BiFeO3 increased the crystallinity of LDPE. Although the crystallinity decreased after magnetization, it was higher than that of LDPE. An AC test showed that the breakdown strength of the composite was higher than that of LDPE. The breakdown strength increased after magnetization. The increase of breakdown strength at high temperature was less, but the breakdown field strength of the composite was higher than that of LDPE. Compared with LDPE, the conductive current of the composite was lower. So, adding BiFeO3 could improve the dielectric properties of LDPE. The current of the composite decayed faster with time. The current decayed slowly after magnetization.
Keywords: BiFeO3/LDPE; electrical properties; magnetization; nanodielectrics.