Monodisperse magnetic γ-Fe2O3 nanoparticles (MNPs) were prepared by a simple, improved, one-pot solvothermal synthesis using SDS and PEG 6000 as double capping reagents. This double protecting layer afforded better MNP uniformity (Z average 257 ± 11.12 nm, PDI = 0.18) and colloidal stability. Materials were characterized by DLS, SEM, TEM, XPS, and XRD. The use of these MNPs in the synthesis of core-shell structures with uniform and tunable silica coatings was demonstrated, as silica coated MNPs are important for use in a range of applications, including magnetic separation and catalysis and as platforms for templated nanogel synthesis.
Keywords: co-precipitation; core–shell nanoparticle; iron-oxide; magnetic nanoparticle; silica coated magnetic nanoparticle; solvothermal; surfactant.