The aim of the article is to analyze the influence of short coir, glass and carbon fiber admixture on the mechanical properties of fly ash-based geopolymer, such as: flexural and compressive strength. Glass fiber and carbon fibers have been chosen due to their high mechanical properties. Natural fibers have been chosen because of their mechanical properties as well as for the sake of comparison between their properties and the properties of the artificial ones. Fourth series of fly ash-based geopolymers for each fiber was cast: 1, 2, and 5% by weight of fly ash and one control series without any fibers. Each series of samples were tested on flexural and compressive strength after 7, 14, and 28 days. Additionally, microstructural analysis was carried out after 28 days. The results have shown an increase in compressive strength for composites with fibers-an improvement in properties between 25.0% and 56.5% depending on the type and amount of fiber added. For bending strength, a clear increase in the strength value is visible for composites with 1 and 2% carbon fibers (62.4% and 115.6%). A slight increase in flexural strength also occurred for 1% addition of glass fiber (4.5%) and 2% addition of coconut fibers (5.4%). For the 2% addition of glass fibers, the flexural strength value did not change compared to the value obtained for the matrix material. For the remaining fiber additions, i.e., 5% glass fiber as well as 1 and 5% coconut fibers, the flexural strength values deteriorated. The results of the research are discussed in a comparative context and the properties of the obtained composites are juxtaposed with the properties of the standard materials used in the construction industry.
Keywords: fibers; geopolymer; mechanical properties.