The design of concrete for radiation shielding structures is principally based on the selection of materials of adequate elemental composition and mix proportioning to achieve the long-term durability in nuclear environment. Concrete elements may become radioactive through exposure to neutron radiation from the nuclear reactor. A selection of constituent materials of greatly reduced content of long-lived residual radioisotopes would reduce the volume of low-level waste during plant decommissioning. The objective of this investigation is an assessment of trace elements with a large activation cross section in concrete constituents and simultaneous evaluation of susceptibility of concrete to detrimental alkali-silica reaction. Two isotopes 60Co and 152Eu were chosen as the dominant long-lived residual radioisotopes and evaluated using neutron activation analysis. The influence of selected mineral aggregates on the expansion due to alkali-silica reaction was tested. The content of 60Co and 152Eu activated by neutron radiation in fine and coarse aggregates, as well as in four types of Portland cement, is presented and discussed in respect to the chemical composition and rock origin. Conflicting results were obtained for quartzite coarse aggregate and siliceous river sand that, despite a low content, 60Co and 152Eu exhibited a high susceptibility to alkali-silica reaction in Portland cement concrete. The obtained results facilitate a multicriteria selection of constituents for radiation-shielding concrete.
Keywords: alkali-silica reaction; concrete durability; low-level radioactive waste; neutron activation analysis; radiation shielding concrete; trace elements.